Performance Index
| Item | Unit | Value |
| ZrO2 | % | 94.5 |
| Y2O3 | % | 5.5 |
| Color | - | white |
| Density | g/cm3 | 6 |
| Water Absorption | % | 0 |
| Rigidity | HRA | 84-87 |
| Bending Resistance | MPa | 1100 |
| Compressive Strength | MPa | 3500 |
| MOE | GPa | 200 |
| Poisson Ratio | - | 0.31 |
| Fracture Toughness | MPa/m | 8 |
| Thermal Expansion | *10-6/°C | 10 |
| Heat Conductivity | W/（m·k） | 3 |
| Working Temperature | °C | <200 |
| HeatShock Resistance | °C | 200 |
| Dielectric Strength | V/m*106 | 11 |
| Volume Resistivity | Ω·cm（20°C）*1014 | 1 |
| Permittivity | - | 33 |
| Dielectric Loss Factor | *10-4 | 520 |
| Nitric Acid | Wt Loss mg/cm2/D | 0.1 |
| Vitriol | Wt Loss mg/cm2/D | 0.5 |
| NaOH | Wt Loss mg/cm2/D | 1 |
| Crystallite Size | μM | <0.6 |